Investigating the thermal stability of the chemical vapour deposited zirconium carbide layers
Loading...
Date
2020
Journal Title
Journal ISSN
Volume Title
Publisher
Journal of Alloys and Compounds
Abstract
The effect of thermal treatment on zirconium carbide (ZrC) layers deposited by chemical vapour deposition
process was investigated using X-ray diffraction (XRD), Raman spectroscopy, nanoindention and
scanning electron microscopy (SEM). The ZrC layers deposited at 1400 C (composed of 96% ZrC and 4% C)
were annealed at 1500, 1600, 1700 and 1800 C for 2 h under high vacuum of 2.6 10 7 mbar. After
annealing, the lattice constant and the average crystallite sizes were found to increase whereas the lattice
strain and dislocation density decreased. The preferred orientation of the as-deposited layers was (220);
it changed to (200) when annealed at 1500 C and 1600 C. At annealing temperature of 1700 C and
1800 C, the preferred orientation was (220) just like for the as-deposited ZrC layers. From Raman
spectroscopy analysis, the ID/IG ratio reduced from 0.694 to 0.414 with annealing temperature indicating
an improvement in crystallinity level and a decrease in the defects in the carbon material in the ZrC
layers. The hardness of the layers was found to decrease slightly with annealing temperature from
26.4 ± 0.6 GPa to 21.3 ± 0.5 GPa. Some voids initially present in the as-deposited ZrC layers closed up and
particles increased in size with annealing temperature.
Description
Keywords
Annealing temperature, Chemical vapour deposition, ZrC layers, Microstructural properties, Surface morphology
Citation
Biira, S., Thabethe, T. T., Hlatshwayo, T. T., Bissett, H., Ntsoane, T., & Malherbe, J. B. (2020). Investigating the thermal stability of the chemical vapour deposited zirconium carbide layers. Journal of Alloys and Compounds, 834, 155003. https://doi.org/10.1016/j.jallcom.2020.155003